Analisis Struktur Kristal Polyetilen Glicol (PEG-4000) Coated Nanopartikel Magnetite (Fe3O4)

The synthesis of materials made from FeSO4.7H2O, FeCl3.6H2O, and NH4OH hydrophilic materials has been carried out using coprecipitation method to produce Fe3O4 nanoparticle material. Analysis of the crystalline structure of Fe3O4 nanoparticles seen from the results of material characterization using X-Ray Diffractometer showed diffraction peaks namely (220) (311) (400) (511) (440) with the main peak at the index (311). Samples of Fe3O4 nanoparticles were modified with PEG-4000 polymer, emerging new diffraction peaks such as peaks with index (111), α- Fe3O4 peaks, γ-FeO (OH) peaks and α-FeO ​​(OH) peaks. The emergence of these new peaks is due to the influence of the PEG-4000 polymer which directly shows the bond with the -OH (hydroxyl) group.Telah dilakukan sintesis material yang berbahan dasar senyawa hidrat FeSO4.7H2O, FeCl3.6H2O, dan NH4OH menggunakan metode kopresipitasi yang menghasilkan material nanopartikel Fe3O4. Analisis struktur kristal nanopartikel Fe3O4 dilihat dari hasil karakterisasi material menggunakan X-Ray Difractometer yang  menunjukkan puncak-puncak difraksi yaitu (220) (311) (400) (511) (440) dengan puncak utama pada indeks (311). Sampel nanopartikel Fe3O4 dimodifikasi dengan polimer PEG-4000, muncul puncak-puncak difraksi yang baru seperti puncak dengan indeks (111), puncak α-Fe3O4, puncak γ-FeO(OH) dan puncak α-FeO(OH). Munculnya puncak-puncak baru tersebut disebabkan oleh pengaruh polimer PEG-4000 yang secara langsung menunjukkan ikatan dengan gugus –OH (hidroksil)