Analisis gugus fungsi pada polimer polyethylene glycol (PEG) coated-nanopartikel oksida besi hitam (Fe3O4) dan biomolekul

A study has been conducted for functional group analysis of polyethylene Glycol (PEG) coated nanoparticles of iron oxide (Fe3O4) and biomolecules using FTIR-Spectroscopy. A sample functional group analysis was performed to determine the ability of modified iron oxide nanoparticles (Fe3O4) with the addition of PEG polymers, potentially to bind biomolecules. The presence of water molecules absorption on the surface of black iron oxide nanoparticles (Fe3O4) causing bonding with PEG polymer is indicated by the absorption peak at the vibration of the -OH (hydroxyl) group at the wave number 3441,01 cm-1. The result of modification of black iron oxide nanoparticles (Fe3O4) with PEG, can bind biomolecules exhibited repetition of the absorption peak on the vibration of the -OH (hydroxyl) group at wave number 3433,29 cm-1 and even the appearance of a new absorption peak on vibration CO at wave number 1350,17 cm-1Telah dilakukan penelitian untuk analisis gugus fungsi pada sampel polimer polyethylene Glicol (PEG) coated- nanopartikel oksida besi hitam (Fe3O4) dan biomolekul menggunakan FTIR-Spectroscopy. Analisis gugus fungsi sampel dilakukan untuk mengetahui kemampuan nanopartikel oksida besi hitam (Fe3O4) yang dimodifikasi dengan penambahan polimer PEG, sangat berpotensi untuk mengikat senyawa biomolekul. Adanya serapan molekul air pada permukaan nanopartikel oksida besi hitam (Fe3O4) yang menyebabkan terjadi ikatan dengan polimer PEG ditunjukkan dengan puncak serapan pada vibrasi gugus –OH (hidroksil) pada bilangan gelombang 3441,01 cm-1. Hasil modifikasi nanopartikel oksida besi hitam (Fe3O4) dengan PEG, dapat mengikat biomolekul ditunjukkan pengulangan puncak serapan pada vibrasi gugus –OH (hidroksil) pada bilangan gelombang 3433,29 cm-1 bahkan munculnya puncak serapan yang baru pada vibrasi gugu C-O pada bilangan gelombang 1350,17 cm-