Sorption comparison of trivalent chromium on various Ficus carica charcoal from tannery wastewater

Content: In this study, equipped charcoal of Ficus carica without impregnation, impregnated with potassium hydroxide (KOH), zinc chloride (ZnCl2) and phosphoric acid (H3PO4) was used for sorption comparison of trivalent chromium from tannery wastewater. The equipped charcoal is characterized before and after used by Fourier transforms infrared spectroscopy (FT-IR). The quantitative elemental analysis is performed of the charcoal using PGT Energy dispersive X-ray spectrometry (EDX). The trivalent chromium sorption efficacy of charcoal was examined investigating charcoal dose, contact time, and relative pH parameters. Batch sorption test revealed that Ficus carica charcoal without impregnation had the maximum sorption capacity of trivalent chromium as depicted Fig. 1a. At the same conditions, trivalent chromium sorption on the Ficus carica charcoal without impregnation, impregnated with potassium hydroxide, zinc chloride and phosphoric acid was 98.9%, 98.8%, 8.9 and 2.5%, respectively. It is noticeable that without impregnation charcoal has a higher sorption capacity. Conversely, impregnation with chemical required cost involvement, time-consuming, long process time, and safe. Fig.1b depicts a shift in the peak intensity which indicated the change of frequency in the functional groups of the charcoal due to chromium adsorption. It indicates various responsible functional groups for the removal of trivalent chromium through Ficus carica charcoal. The trivalent chromium removal efficiency with the Ficus carica charcoal without impregnation was achieved 98.9%. The study could be helpful to design the sorption of trivalent chromium from the tannery wastewater in-house prior to discharge. Take-Away: 1. Without impregnation, Ficus carica charcoal has a better trivalent chromium sorption capacity 2. Trivalent chromium sorption capacity was 98.9