SIFAT TERMAL DAN KELARUTAN DARI CYCLIC LIQUID NATURAL RUBBER

Cyclic Liquid Natural Rubber (CLNR) is a cyclical natural rubber which has decreased molecular weight. Synthesis of Cyclic Liquid Natural Rubber (CLNR) can be done in a way that degradation after cyclization. Degradation after cyclization using Cyclic raw material Natural rubber (CNR), the degradation is done by using phenylhydrazine reagents with oxygen gas atmosphere with a flow rate of 2 LMenit-1 for 24 hours. CNR and CLNR thermal analysis by DSC, Tg results obtained amounted to 102.82 ° C and 103.67 ° C, Tc amounted to 362.45 ° C and 330.29 ° C and Tm mounted to 509.24 ° C and 440 , 00 oC. Of CNR and CLNR solubility test has a polarity index of 2.4 to 4.4 and from 2.4 to 4.4.Cyclic Liquid Natural Rubber (CLNR) adalah karet alam siklis yang telah mengalami penurunan berat molekul. Sintesis Cyclic Liquid Natural Rubber (CLNR) dapat dilakukan dengan cara yaitu degradasi setelah siklisasi. Degradasi setelah siklisasi menggunakan bahan baku Cyclic Natural Rubber (CNR), degradasi dilakukan dengan bantuan reagen phenylhydrazine dengan suasana gas oksigen dengan laju alir 2 LMenit-1 selama 24 jam. Analisa termal CNR dan CLNR dengan DSC diperoleh hasil Tg masing – masing sebesar 102,82 oC dan 103,67 oC, Tc masing – masing sebesar 362,45 oC dan 330,29 oC dan Tm masing – masing sebesar 509,24 oC dan 440,00 oC. Dari uji kelarutan CNR dan CLNR memiliki indeks kepolaran dari 2,4 – 4,4 dan 2,4 – 4,4