Ciclo térmico para la obtención de una ferrita de Ni-Zn: (II) Influencia de la etapa de enfriamiento

Ceramic bodies formed from (Cu0.12Ni0.23Zn0.65)Fe2O4 ferrite powders stand out as electromagnetic radiation absorbers among Cu-doped Ni-Zn ferrites, preventing interference between electronic devices. In a preliminary study, a methodology was established for designing the sintering stage of a thermal cycle, which allows the foregoing ceramic bodies to be obtained with the appropriate microstructure (high relative density and little grain growth) to provide them with good electromagnetic properties. The present study examines the cooling stage (i.e. the stage following the sintering stage) of that thermal cycle and the influence of the cooling rate on fired relative density, average grain size, and grain size distribution, varying the sintering time of the thermal cycle used.<br><br>Las piezas cerámicas obtenidas a partir de polvos de ferritas de composición (Cu0.12Ni0.23Zn0.65)Fe2O4 destacan como absorbentes de radiación electromagnética entre las ferritas de Ni-Zn dopadas con Cu, impidiendo interferencias entre dispositivos electrónicos. En un trabajo previo se estableció la metodología para diseñar la etapa de sinterización de un ciclo térmico que permite obtener las piezas cerámicas mencionadas con una microestructura adecuada (elevada densidad relativa y escaso crecimiento de grano) para que presenten unas buenas propiedades electromagnéticas. En este trabajo se ha estudiado la etapa de enfriamiento del mismo ciclo térmico (etapa siguiente a la de sinterización), determinando la influencia que ejerce la velocidad de enfriamiento sobre la densidad relativa en cocido, el tamaño medio de grano y la distribución de tamaños de grano, variando el tiempo de sinterización del ciclo térmico empleado