Clean production of corn stover pulp using KOH+NH4OH solution and its kinetic during delignification

The self-made KOH together with NH4OH pulping of corn stover was investigated. The combined alkaline system could effectively remove lignin during pulping. There are three stages of lignin removal during delginification. Approximately 90% of lignin could be removed after temperature reached 150ºC for over 30 minutes. The p-hydroxyl phenol groups in lignin could be completely removed during the delignification reaction. The tendency of the increase of the crystalline degree of cellulose is observed with increase of reaction temperature. The kinetics of delignification is found to be the first order with respect to the remained lignin and the 0.4 order with respect to the remained hydroxide concentration. The activation energy of delignification is 23 kJ/mol. The solution obtained from precipitation of lignin is rich in nitrogen, phosphorous, potassium elements and organic matters. Various techniques including FT-IR, GPC, DSC, were applied to characterize the acid precipitated lignin. The result shows that the lignin with the polydispersity of 1.4 still maintains the p-coumaryl, coniferyl, and sinapyl units in its matrix