Fracture analysis of chilled cast iron camshaft

The fracture of a camshaft made of chilled cast iron, installed in a home-made Fukang car, happened only after running over a distance of 6,200 km. The fractured camshaft was received to conduct a series of failure analyses using visual inspection, SEM observation of fracture section, microstructure analysis, chemical composition analysis and hardness examination and so on, while those of CKD camshaft made by Citro雗 Company in France was also simultaneously analyzed to compare the difference between them. The results showed that the fracture of the camshaft mainly results from white section in macrostructure and Ledeburite in microstructure; the crack in the fractured camshaft should be recognized to initiate at the boundary of coarser needle-like carbide and matrix, and then propagate through the transverse section. At the same time, the casting defects such as dendritic shrinkage, accumulated inclusion and initiated crack and abnormal external force might stimulate the fracture of camshaft as well. Based on failure analysis, some measures have been employed, and as a result, the fracture of home-made camshafts has been effectively prevented