Understanding the leaching behavior of inorganic polymers made of iron rich slags

This study investigates the leaching of main and trace elements from inorganic polymers made with an iron rich, fumed, > 90% amorphous slag. Different inorganic polymer binders were synthesized, varying the amount of the activating solution and the silica over sodium oxide ratio from 1.6, to 1.8, to 2.0, with constant water content of ±63%. Cascade and column leaching tests were performed in combination with geochemical speciation modeling (Visual MINTEQ) with the aim to understand the speciation of the elements in the inorganic polymer and their leaching behaviour as a function of pH. This would allow to identify the elements which would be the major issue with respect to leaching when the slag will be used in a construction material. The formed inorganic polymer was able to immobilize cationic elements such as barium, copper, magnesium, manganese, and zinc, in the pH range 7–12.5 due to adsorption. Elements such as antimony, arsenic, phosphorus, molybdenum, and vanadium were easily leached out in column and cascade leaching tests, because they most likely occurred as anions in the pore solution. Lead, chromium, and titanium were immobilized in the binder or in crystalline phases in the pH range 3.5–12.5. The study shows that there are multiple factors that affect leaching, the most important of which is shown to be the nature (cationic or anionic) of the elements and the morphology of the matrix. Anions that are present as trace elements (