High-temperature deformation properties of CuCr0.6 alloy

The submitted paper aimed to investigate the hot deformation behavior of CuCr0.6 alloy. Nil strength temperature of 1349 K and nil ductility temperature of 1313 K have been experimentally determined. Formability is monotonously increased with the decrease of forming temperature in the temperature range from 923 K to approx. 1273 K. The flow stress curves were obtained in the forming temperature interval of 923-1223 K and at a strain rate of 0.1-10 s(-1). After their analysis, the hot deformation activation energy of 340 kJ mol(-1) was calculated for peak stress and 393 kJ mol(-1) for steady state. This proves that the value of the activation energy depends upon a strain size.Web of Science57641440