Preparing titanium dioxide from titania-rich slag(TiO_2 73wt%) by molten NaOH method has been developed.The effects of tem-perature and reaction time on the titanium conversion were investigated.The results showed that temperature had significant influence on the titanium conversion as well as the structure of the product.About 92% of titanium in the titania-rich slag could be converted after reacting with NaOH at 500℃ for 1 h.Metatitanic acid was formed through the steps of washing treatment,acid dissolution,and hydrolysis.Well-dispersed spherical titanium dioxide particles with an average size of 0.1-0.4 μm can be obtained by calcination of metatitanic acid.In addition,the content of titanium dioxide in the product is up to 98.6wt%,which ...
Titanium slags produced through ilmenite electric furnace smelting contain 60–80%TiO2, a vital titan...
An alternative route was proposed for preparing rutile titanium dioxide (TiO2) white pigment. The pr...
This article presents studies on the ammonium fluoride processing of dusts from the reduction smelti...
Preparing titanium dioxide from titania-rich slag (TiO2 73wt%) by molten NaOH method has been develo...
A novel method of caustic hydrothermal decomposition of titanium slag followed by acidification of t...
The titanium dioxide(TiO<sub>2</sub>) was prepared by efficient decomposition of titanium- bearing b...
The caking and adhesion of intermediate product on reactor surfaces during TiO2 production via the N...
A novel process was proposed for preparing titanium dioxide by the decomposition of titanium slag in...
In recent few years the production of high titanium slags has become a major industrial operation ; ...
The titanium dioxide(TiO2) was prepared by efficient decomposition of titanium- bearing blast furnac...
TiO2 is an important inorganic material which is commercially produced by either the chloride or the...
TiO2 is an important inorganic material which is commercially produced by either the chloride or the...
Rutile titanium dioxide (TiO2) white pigment is prepared by a novel NaOH molten-salt process. Titani...
The titanium dioxide(TiO2) was prepared by efficient decomposition of titanium- bearing blast furnac...
The present work provides a method for beneficiating of an Egyptian titanium slag by a thermal oxida...
Titanium slags produced through ilmenite electric furnace smelting contain 60–80%TiO2, a vital titan...
An alternative route was proposed for preparing rutile titanium dioxide (TiO2) white pigment. The pr...
This article presents studies on the ammonium fluoride processing of dusts from the reduction smelti...
Preparing titanium dioxide from titania-rich slag (TiO2 73wt%) by molten NaOH method has been develo...
A novel method of caustic hydrothermal decomposition of titanium slag followed by acidification of t...
The titanium dioxide(TiO<sub>2</sub>) was prepared by efficient decomposition of titanium- bearing b...
The caking and adhesion of intermediate product on reactor surfaces during TiO2 production via the N...
A novel process was proposed for preparing titanium dioxide by the decomposition of titanium slag in...
In recent few years the production of high titanium slags has become a major industrial operation ; ...
The titanium dioxide(TiO2) was prepared by efficient decomposition of titanium- bearing blast furnac...
TiO2 is an important inorganic material which is commercially produced by either the chloride or the...
TiO2 is an important inorganic material which is commercially produced by either the chloride or the...
Rutile titanium dioxide (TiO2) white pigment is prepared by a novel NaOH molten-salt process. Titani...
The titanium dioxide(TiO2) was prepared by efficient decomposition of titanium- bearing blast furnac...
The present work provides a method for beneficiating of an Egyptian titanium slag by a thermal oxida...
Titanium slags produced through ilmenite electric furnace smelting contain 60–80%TiO2, a vital titan...
An alternative route was proposed for preparing rutile titanium dioxide (TiO2) white pigment. The pr...
This article presents studies on the ammonium fluoride processing of dusts from the reduction smelti...