Utilization of geothermal water as irrigation water after boron removal by monodisperse nanoporous polymers containing NMDG in sorption-ultrafiltration hybrid process

WOS: 000353094300007A relatively new method of polymerization, 'modified seeded polymerization' has been used for the synthesis of monodisperse nanoporous poly(glycidyl methacrylate-co-ethylene dimethacrylate) and poly(vinylbenzyl chloride-co-divinylbenzene) beads. The synthesized polymer beads were then functionalized with N-methyl-D-glucamine (NMDG) to obtain boron selective resins. The efficiency of these particles for boron removal from geothermal water was investigated by using the hybrid process coupling sorption with ultrafiltration (UF) method where a submerged hollow fiber type UF membrane module was employed for filtration. It was possible to reduce the boron concentration from 11.0 mg/L to <= 1 mg/L in 20 min with hybrid method using poly(glycidyl methacrylate-co-ethylene dimethactylate)-NMDG beads with 4 g-resin/L-geothermal water. The respective period for poly(vinylbenzyl chloride-co-divinylbenzene) beads with the same resin dosage was 30 min. In the case of commercially available boron selective ion exchange resin Dowex-XUS 43594.00 ground to an average particle size of 20 pm, the target boron concentration which is mg/L was reached in 20 mm by using 2 g-resin/L-geothermal water. (C) 2015 Elsevier B.V. All rights reserved.National Boron Research Institute, BORENMinistry of Energy & Natural Resources - Turkey [2008-G-0192]; TUBITAKTurkiye Bilimsel ve Teknolojik Arastirma Kurumu (TUBITAK)This work was supported financially by the National Boron Research Institute, BOREN (Project Number: 2008-G-0192). We are grateful also to TUBITAK for the post-doc fellowship to Dr. S. Samatya. We thank E. Guler for the kind help to run hybrid tests. We thank Dow Chemical Co. for sending us boron selective resins Dowex-XUS-43594.00 as a gift