Add to ORKGPrinted copies available from the following: The use of trademarks or names of manufacturers in this report is for accurate reporting and does not constitute an official endorsement, either expressed or implied, of such products or manufacturers by the National Aeronautics and Space Administration
Aerospace structures are optimally designed and analyzed to specifically-defined engineering paramet...
In the initial phase of a NACA program on fatigue research, axial-load tests on 24S-T3 and 75S-T6 al...
In the present investigation aluminium Alclad 2024-T3 sheet material was tested. The aim of this inv...
An experimental study was conducted to determine the effects of combined bending and membrane cyclic...
An experimental study was conducted to determine the effects of combined bending and membrane cyclic...
Fatigue crack propagation has been observed for a number of commercial aluminium alloys. Comparable ...
Static tensile tests were performed on simple notched specimens containing fatigue cracks. Four type...
A series of fatigue tests with specimens subjected to constant amplitude and two-step axial loads we...
Stress ratio effects on fatigue crack growth in sheet aluminum alloys.Prepared at Langley Research C...
The aim of this study was to investigate the failure mechanism of riveted aluminium lap joints when ...
In the initial phase of an NACA program on fatigue research, axial-load tests on 24S-T3 and 75S-T6 a...
In an aircraft structure, fatigue failures usually started from the initiation and propagation of cr...
The purpose of this experiment was to observe fatigue failure using a rotating fatigue (Wohler) mach...
Aluminum components manufactured from sheet metal are used in numerous applications including electr...
Aluminum alloy 6061 (AA 6061) finds various usage as structural material. Nowaday, metal matrix comp...
Aerospace structures are optimally designed and analyzed to specifically-defined engineering paramet...
In the initial phase of a NACA program on fatigue research, axial-load tests on 24S-T3 and 75S-T6 al...
In the present investigation aluminium Alclad 2024-T3 sheet material was tested. The aim of this inv...
An experimental study was conducted to determine the effects of combined bending and membrane cyclic...
An experimental study was conducted to determine the effects of combined bending and membrane cyclic...
Fatigue crack propagation has been observed for a number of commercial aluminium alloys. Comparable ...
Static tensile tests were performed on simple notched specimens containing fatigue cracks. Four type...
A series of fatigue tests with specimens subjected to constant amplitude and two-step axial loads we...
Stress ratio effects on fatigue crack growth in sheet aluminum alloys.Prepared at Langley Research C...
The aim of this study was to investigate the failure mechanism of riveted aluminium lap joints when ...
In the initial phase of an NACA program on fatigue research, axial-load tests on 24S-T3 and 75S-T6 a...
In an aircraft structure, fatigue failures usually started from the initiation and propagation of cr...
The purpose of this experiment was to observe fatigue failure using a rotating fatigue (Wohler) mach...
Aluminum components manufactured from sheet metal are used in numerous applications including electr...
Aluminum alloy 6061 (AA 6061) finds various usage as structural material. Nowaday, metal matrix comp...
Aerospace structures are optimally designed and analyzed to specifically-defined engineering paramet...
In the initial phase of a NACA program on fatigue research, axial-load tests on 24S-T3 and 75S-T6 al...
In the present investigation aluminium Alclad 2024-T3 sheet material was tested. The aim of this inv...