Cation distribution and magnetic structure of the ferrimagnetic spinel NiCo2O4

The compound NiCo2O4, with spinel-related structure, has been prepared by thermal decomposition of metal nitrates and its bulk structural properties examined by means of magnetic measurements, neutron diffraction, X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS). The results suggest a delocalised electron distribution on the octahedral sites with average oxidation states of +3.5 and +2.5 for nickel and cobalt, respectively, and lead to a cation distribution for NiCo2O4 of (Ni3+0.1Co2+0.9)tet [Ni3.5+0.9Co2.5+1.1] octO4. This electronic configuration is consistent with magnetisation measurements if applied magnetic fields cause a charge redistribution on the octahedral sites to favour Co3+ and Ni3+. The surface of NiCo2O4 was examined by X-ray photoelectron spectroscopy (XPS) and found to have a different composition containing Co2+, Co3+, Ni2+, Ni3+ and, probably, Ni4+