Add to ORKGThis article investigates the effect of polyurethan (PU) resin as a binding agend for wood fiber (WF)_ and palm kernel shell (PKS) composite boardl in terms of physical and mechanical properties. A series of fiberboard samples consisting of WF/PKS at a ratio of 85/15 with different percentage of PU adhesive (40%, 50% and 60%) have been fabricated. The results showed that flexural modulus, flexural strength, tensile modulus, tensile strength and hardness of the boards were increased with the increase of PU adhesive percentage. The effects of the binder were also explained in terms of porosity and surface morphology. Based on the results, the board met the Japanese Industrial Standard A 5905 for type 5 and can be classified as medium densit...
The purpose of this study was to develop core composite materials using veneer residues combined wit...
Palm kernel oil was used as a raw material for the synthesis of polyester polyol.The palm oil based ...
The extensibility and strength of fibre networks can be improved by modifying fibre material mechani...
This article investigates the effect of polyurethan (PU) resin as a binding agend for wood fiber (WF...
The oil palm industry has brought significant impacts to the economy, social, geographical as well a...
In Malaysia, the oil palm industry has brought significant impacts to the economy, social, geograph...
The high demand for wood-based composites generates a greater use of wood adhesives. The current ind...
Three layers of wood-based composites of planed lumber-UHMWPE-veneer structure were prepared using p...
In this research, the effect of increasing content of urea to urea-formaldehyde adhesive on physical...
In this investigation the effect of using of UF and MUF Resins on Physical and mechanical Properties...
Incorporating biodegradable reinforcement, such as wood particles, into rigid polyurethane foams (RP...
In this investigation, the effect of mat moisture content, press temperature and time on polymerizat...
The objective of this study was to manufacture a lightweight and easily producible wood plastic lami...
The objective of this study was to evaluate the best parameters of particleboard manufacturing throu...
This paper presents a study on the potential use of coconut fiber as material to produce particleboa...
The purpose of this study was to develop core composite materials using veneer residues combined wit...
Palm kernel oil was used as a raw material for the synthesis of polyester polyol.The palm oil based ...
The extensibility and strength of fibre networks can be improved by modifying fibre material mechani...
This article investigates the effect of polyurethan (PU) resin as a binding agend for wood fiber (WF...
The oil palm industry has brought significant impacts to the economy, social, geographical as well a...
In Malaysia, the oil palm industry has brought significant impacts to the economy, social, geograph...
The high demand for wood-based composites generates a greater use of wood adhesives. The current ind...
Three layers of wood-based composites of planed lumber-UHMWPE-veneer structure were prepared using p...
In this research, the effect of increasing content of urea to urea-formaldehyde adhesive on physical...
In this investigation the effect of using of UF and MUF Resins on Physical and mechanical Properties...
Incorporating biodegradable reinforcement, such as wood particles, into rigid polyurethane foams (RP...
In this investigation, the effect of mat moisture content, press temperature and time on polymerizat...
The objective of this study was to manufacture a lightweight and easily producible wood plastic lami...
The objective of this study was to evaluate the best parameters of particleboard manufacturing throu...
This paper presents a study on the potential use of coconut fiber as material to produce particleboa...
The purpose of this study was to develop core composite materials using veneer residues combined wit...
Palm kernel oil was used as a raw material for the synthesis of polyester polyol.The palm oil based ...
The extensibility and strength of fibre networks can be improved by modifying fibre material mechani...