Add to ORKGSmall specimens (3.2-mm thick) of Douglas-fir heartwood were tested for mechano-sorptive (MS) deformation in tangential tension during moisture adsorption. Tests were made at 65.5° with moisture content (MC) changing from 5 to 20% under four levels of stress: 0.276, 0.552, 0.827, and 1.24 MPa. The results confirmed that a large MS deformation occurs during the first MC increase after the load is applied. In a sorplion history of matched loaded and load-free specimens, the MS strain was shown to be proportional to applied stress, and the material parameters describing the interaction of stress and moisture change were independent of stress level
Collapse and drying stresses are currently induced during the drying of Eucalyptus nitens in solid w...
Collapse and drying stresses are currently induced during the drying of Eucalyptus nitens in solid w...
To provide comprehensive data on creep behaviors at relative humidity (RH) isohume conditions and fi...
Small specimens (3.2-mm thick) of Douglas-fir heartwood were tested for mechano-sorptive (MS) deform...
This work presents the phenomenon of mechano-sorptive strain in the deformation of wood during moist...
The effect of tensile and compressive stresses on northern red oak, in the radial and tangential dir...
This research confirms that, at a given equilibrium moisture content, the strength perpendicular to ...
The principal objective of the project was to provide a reliable testing protocol for determination ...
Samples of nine tropical hardwoods from Peru and sugar maple wood from Quebec were selected to under...
Graduation date: 2010Hygro-mechanical effect is a general term applied to all phenomena that involve...
The effects on wood of simultaneous mechanical and moisture loading are studied. In order to clarify...
Graduation date: 1994Presentation date: 1993-07-01Large inelastic strain occurs inside a piece of lu...
The purpose of this work is to show the magnitude of mechanosorptive creep compared to ordinary visc...
The effects on wood of simultaneous mechanical and moisture loading are studied. In order to clarify...
The purpose of this paper was to determine the mechano-sorptive strains produced during desorption o...
Collapse and drying stresses are currently induced during the drying of Eucalyptus nitens in solid w...
Collapse and drying stresses are currently induced during the drying of Eucalyptus nitens in solid w...
To provide comprehensive data on creep behaviors at relative humidity (RH) isohume conditions and fi...
Small specimens (3.2-mm thick) of Douglas-fir heartwood were tested for mechano-sorptive (MS) deform...
This work presents the phenomenon of mechano-sorptive strain in the deformation of wood during moist...
The effect of tensile and compressive stresses on northern red oak, in the radial and tangential dir...
This research confirms that, at a given equilibrium moisture content, the strength perpendicular to ...
The principal objective of the project was to provide a reliable testing protocol for determination ...
Samples of nine tropical hardwoods from Peru and sugar maple wood from Quebec were selected to under...
Graduation date: 2010Hygro-mechanical effect is a general term applied to all phenomena that involve...
The effects on wood of simultaneous mechanical and moisture loading are studied. In order to clarify...
Graduation date: 1994Presentation date: 1993-07-01Large inelastic strain occurs inside a piece of lu...
The purpose of this work is to show the magnitude of mechanosorptive creep compared to ordinary visc...
The effects on wood of simultaneous mechanical and moisture loading are studied. In order to clarify...
The purpose of this paper was to determine the mechano-sorptive strains produced during desorption o...
Collapse and drying stresses are currently induced during the drying of Eucalyptus nitens in solid w...
Collapse and drying stresses are currently induced during the drying of Eucalyptus nitens in solid w...
To provide comprehensive data on creep behaviors at relative humidity (RH) isohume conditions and fi...