ПСЕВДОНЕПОЛНОЕ СМАЧИВАНИЕ ГРАНИЦ ЗЕРЕН В СИЛЬНОДЕФОРМИРОВАННЫХ СПЛАВАХ Al–Zn

Al–Zn alloys after the intense plastic deformation by the high-pressure torsion method have three various classes of grain boundaries (GBs) Al/Al wetted with a second zinc-enriched phase. Completely wetted Al/Al GBs are coated with a layer of the zinc-enriched phase thicker than 30 nm. Partially (incompletely) wetted Al/Al GBs contact with particles of the zinc-enriched phase with a contact angle >60° but contain no any measurable zinc concentration. Pseudopartially wetted Al/Al GBs also contact with Zn particles with a contact angle >60°. However, they have a thin interlayer of the zinc-enriched phase with a uniform thickness of 2–4 nm, the presence of which explains the unusually high plasticity of the Al–Zn alloys after highpressure torsion.Сплавы Al–Zn после интенсивной пластической деформации методом кручения под высоким давлением имеют три различных класса границ зерен (ГЗ) Al/Al, смоченных второй твердой фазой, богатой цинком. Полностью смоченные ГЗ Al/Al покрыты слоем фазы, обогащенной цинком, толщиной более 30 нм. Частично (не полностью) смоченные ГЗ Al/Al контактируют с частицами фазы, богатой цинком, с контактным углом >60°, но не содержат какой-либо измеримой концентрации цинка. Псевдонеполно смоченные ГЗ Al/Al также контактируют с частицами Zn с углом контакта >60°. Тем не менее они имеют тонкую прослойку фазы, богатой цинком, равномерной толщины 2–4 нм, наличие которой объясняет необычайно высокую пластичность сплавов Al–Zn после кручения под высоким давлением