Magnetic hysteresis in granular CuCo alloys

Room-temperature hysteresis loops of granular Cu100-xCox alloys (5 less than or equal to x less than or equal to 15) obtained by planar flow casting in air and submitted to proper annealing treatments have been measured up to a field of 10 kOe by means of a vibrating sample magnetometer. In major loops (\H-vert\ = 10 kOe), the reduced remanence-to-saturation ratio m(r) = M-r/M-s and the coercivity H-c measured on all studied materials appear to be related by an almost linear law of the type m(r) approximate to 1/3 (mu H-c/kT), mu being the average magnetic moment on Co particles. A similar relation is also observed on minor symmetrical loops (100 Oe less than or equal to\H-vert\ less than or equal to 9 kOe). The observed results are accounted for by a model which considers the hysteresis as originating by magnetic interactions among nearly superparamagnetic Co particles. (C) 1999 American Institute of Physics. [S0021-8979(99)51408-4]