Fabrication of short carbon fibre reinforced SiC multilayer composites by tape casting

Silicon carbide multilayer composites containing short carbon fibres (Csf/SiC) were prepared by tape casting and pressureless sintering. C fibres were dispersed in solvents and then mixed with SiC slurry to make green Csf/SiC tape. Triton X-100 was found to be the best one for Toho Tenax HTC124 fibres (with water soluble coating) among BYK-163, BYK-410, BYK-2150, BYK-9076, BYK-9077 and Triton X-100 dispersants. Csf/SiC multilayer composites containing 5 vol.% fibres (mean fibre length of 3, 4.5, and 6 mm) were obtained. Addition of short C fibres seems to worsen the densification process in the Csf/SiC multilayer composites, whereas anisotropy shrinkage in Csf/SiC was also observed. Open pores size was increased slightly after the addition of C fibre but it decreased with the mean fibre length. Mechanical properties were affected by high residual porosity. The addition of short C fibres has not changed the crack deflection at weak interfaces. Csf/SiC multilayer composites containing longer fibres (4.5 and 6 mm) presented higher elastic modulus, bending strength and Vickers hardness as compared to shorter fibres (3 mm). Improved sintering performance and fibre content are necessary to improve mechanical properties