Propiedades de geopolímeros preparados a partir de cenizas de estanque

Alkali-activated materials were prepared from pond ash from the Darkhan city (Mongolia) thermal power station. This ash contains about 60 wt % X-ray amorphous material in addition to quartz, mullite, hematite and magnesioferrite, and presents significant storage problems since it is accumulating in large amounts and is a hazardous waste, containing 90–100 ppm of the heavy metals As, Pb and Cr, and about 800 ppm Sr. Alkali-activated materials synthesized from the as-received pond ash achieved compressive strengths of only 3.25 MPa. Reduction of the particle size by mechanical milling for up to 30 min progressively increases the compressive strength of the resulting alkali-activated geopolymer up to 15.4 MPa. Leaching tests indicate that the combination of milling and alkali treatment does not cause the release of the hazardous heavy metals from the product, making it suitable for construction applications.Se prepararon materiales activados alcalinamente a partir de cenizas de charca de la central térmica de Darkhan (Mongolia). Esta ceniza contiene alrededor de un 60% en peso de material amorfo además de mullita, hematita, cuarzo y magnesioferrite. Presenta además importantes problemas de almacenamiento ya que se acumula en grandes cantidades y es un desecho peligroso, que contiene entre 90–100 ppm de metales pesados como Pb y Cr, y alrededor de 800 ppm de Sr. Los materiales sintetizados a partir de las cenizas de estanque presentaron resistencias a compresión de tan sólo 3,25 MPa. La reducción del tamaño de partícula por fresado mecánico hasta 30 min aumentó las resistencias mecánicas hasta valores de 15.4 MPa. Las pruebas de lixiviación indican que la combinación de molienda y activación alcalina no causan la liberación de los metales pesados peligrosos del producto, por lo que resulta adecuado para aplicaciones en construcción