Influencia de la adición del BaCO3 sobre la hidratación del cemento portland

The effect of incorporation of BaCO3 in portland cement hydration has been studied. From this study it is inferred that presence of BaCO3 in cements makes them require a higher quantity of mixing water. However, mechanical resistances do not seem negatively affected, for a formation of carboaluminates by chemical reaction between the barium carbonate and the C3A of the clinker appears. The BaCO3 reveals a retardant effect on the setting time, in presence of gypsum as much as in its absence. The BaCO3 with gypsum reacts as BaSO4, a salt of a very high stability. The formation of this barium salt inhibits the formation of ettringite in pastes. Finally, the presence of BaCO3 in cements ensures that no expansive process will occur in sulphatic means either external or internal, for carbonate is going to react with these sulphates and form BaSO4, preventing thus the formation of expansive ettringite.Se ha estudiado el efecto de la incorporación de BaCO3 en la hidratación del cemento portland. Como resultado del estudio se ha concluido que la presencia de BaCO3 en los cementos hace que éstos requieran una mayor cantidad de agua de amasado. Sin embargo, las resistencias mecánicas no se ven negativamente afectadas, ya que se produce la formación de carboaluminatos por reacción química entre el carbonato de bario y el C3A del clinker. El BaCO3 manifiesta un efecto retardador en los tiempos de fraguado, tanto en presencia como en ausencia de yeso. El BaCO3 reacciona con el yeso formando BaSO4, sal de muy elevada estabilidad. La formación de esta sal de bario inhibe la formación de ettringita en las pastas. Finalmente, indicar que la presencia de BaCO3 en los cementos asegura que éstos no experimenten procesos expansivos cuando se encuentren en medios sulfáticos externos o internos, ya que el carbonato interaccionará con dichos sulfatos formando BaSO4 e impidiendo la formación de ettringita expansiva