On the micro- and macroscopic elastoplastic deformation behaviour of cast iron when subjected to cyclic loading

The complicated constitutive behaviour of cast iron, involving a non-linear elastic regime, tension-compression stress asymmetry, varying elastic modulus and an inflection in the tension-to-compression hardening curve, is investigated using a micromechanical modelling approach. In this way, it is demonstrated that the abnormalities observed in the constitutive behaviour are qualitatively and quantitatively explained by the interaction behaviour between the matrix and graphite constituents. In initial tension, the absence of linearity is rationalised by the successive loss in load-carrying capacity of the graphite phase due to debonding, which in subsequent cycling, results in the opening and re-contact of the matrix-graphite interface. This effect is demonstrated to result in tension-compression asymmetry in stress and elastic modulus, as well as the inflection in tension-to-compression loading. The given model of explanation is validated by comparison to the experimentally acquired microscopic strain field in EN-GJV-400 at locations where stress concentrations are generated due to the matrix-graphite debonding, using high-resolution digital image correlation of scanning electron images.Funding Agencies|Scania CV AB; Swedish Governmental Agency for Innovation Systems [FFI - 2012 - 03625]; Swedish Foundation for Strategic Research [SM12 - 0014]; Strategic Faculty Grant AFM (SFO - MAT - LiU) at Linkoping University [2009 -00971]