Add to ORKGPolyamide 6/clay nanocomposites of various clay concentrations were prepared by a single screw mixing extruder. The structure and morphology of nanocomposites were studied by X-ray diffraction (XRD), transmission electron microscopy (TEM). It was found that complete exfoliation of clay in PA 6 matrix was occurred at all clay concentrations as detected by TEM studies and disappearance of clay peak in XRD. An order of magnitude improvement in oxygen permeability was observed by increasing concentration clay
The degradation pathway of polyamide 6/clay nanocomposites was studied as a function of clay content...
390-401Using maghnite as an inorganic reinforcement, polyamide-6-based nanocomposites (PA6/Mag-CTA) ...
Polymer-layered silicate nanocomposites based on polyamide, thermoplastic polyurethane, and polyole...
Polyamide 6 (PA6)/clay nanocomposites, based on organo-modified and pristine (i.e. purified but non-...
Polymer/clay nanocomposites are materials composed of a polymer matrix and nanometer size clay parti...
In this research, the influence of auto-thermal extrusion on the thermal stability and morphology of...
Polyamide 6 (PA6)/clay nanocomposites were prepared using a single screw extruder with an ultrasonic...
This work aims at comparing the efficiency of three melt compounding methods for preparing polyamide...
The main purpose of this thesis is to study the influence of auto thermal extrusion on the thermal s...
In this thesis, the effect of screw speed and temperature profile during the extrusion of polyamide ...
Polyamide-6 nanocomposites were prepared from a new phosphonium organoclay obtained at pilot scale i...
Polyamide 6 and pristine montmorillonite have been melt blended in an extruder and water was injecte...
Nylon 66/clay nanocomposites were prepared in a Berstorff ZE25A UTX Ultra-glide corotating twin scre...
International audienceThe influence of the incorporation of nanoparticles (organo-modified montmoril...
Bio-based polymers and polymer nanocomposites have known an increasing interest during the past few ...
The degradation pathway of polyamide 6/clay nanocomposites was studied as a function of clay content...
390-401Using maghnite as an inorganic reinforcement, polyamide-6-based nanocomposites (PA6/Mag-CTA) ...
Polymer-layered silicate nanocomposites based on polyamide, thermoplastic polyurethane, and polyole...
Polyamide 6 (PA6)/clay nanocomposites, based on organo-modified and pristine (i.e. purified but non-...
Polymer/clay nanocomposites are materials composed of a polymer matrix and nanometer size clay parti...
In this research, the influence of auto-thermal extrusion on the thermal stability and morphology of...
Polyamide 6 (PA6)/clay nanocomposites were prepared using a single screw extruder with an ultrasonic...
This work aims at comparing the efficiency of three melt compounding methods for preparing polyamide...
The main purpose of this thesis is to study the influence of auto thermal extrusion on the thermal s...
In this thesis, the effect of screw speed and temperature profile during the extrusion of polyamide ...
Polyamide-6 nanocomposites were prepared from a new phosphonium organoclay obtained at pilot scale i...
Polyamide 6 and pristine montmorillonite have been melt blended in an extruder and water was injecte...
Nylon 66/clay nanocomposites were prepared in a Berstorff ZE25A UTX Ultra-glide corotating twin scre...
International audienceThe influence of the incorporation of nanoparticles (organo-modified montmoril...
Bio-based polymers and polymer nanocomposites have known an increasing interest during the past few ...
The degradation pathway of polyamide 6/clay nanocomposites was studied as a function of clay content...
390-401Using maghnite as an inorganic reinforcement, polyamide-6-based nanocomposites (PA6/Mag-CTA) ...
Polymer-layered silicate nanocomposites based on polyamide, thermoplastic polyurethane, and polyole...