PENGARUH IRADIASI-γ TERHADAP REGANGAN KISI DAN KONDUKTIVITAS IONIK PADA KOMPOSIT PADAT (LiI)0,5(Al2O3.4SiO2)0,5

ABSTRAK PENGARUH IRADIASI-γ TERHADAP REGANGAN KISI DAN KONDUKTIVITAS IONIK PADA KOMPOSIT PADAT (LiI)0,5(Al2O3.4SiO2)0,5. Komposit padat (LiI)0,5(Al2O3.4SiO2)0,5 telah dapat dibuat dengan pencampuran antara LiI dengan Al2O3.4SiO2. Komposit padat di pelet dengan ukuran diameter 1,5 cm dan tekanan 5000 psi. Kemudian komposit padat tersebut dilakukan iradiasi dengan dosis 100 kGy, 200 kGy, 300 kGy dan 400 kGy. Pengukuran struktur kristal dilakukan dengan teknik difraksi sinar-x. Dari pola difraksi sinar-x pada komposit (LiI)0,5(Al2O3.4SiO2)0,5 menunjukkan bahwa struktur yang terbentuk adalah campuran struktur LiI dan Al2O3.4SiO2. Regangan kisi komposit (LiI)0,5(Al2O3.4SiO2)0,5 menurun seiring dengan naiknya dosis radiasi. Pengukuran konduktivitas dilakukan dengan alat LCR pada kisaran frekuensi 0,1 Hz-100 kHz. Konduktivitas komposit (LiI)0,5(Al2O3.4SiO2)0,5 menurun seiring dengan naiknya dosis radiasi. Kata kunci: Elektrolit padat, iradiasi, difraksi sinar-x , konduktivitas. ABSTRACT EFFECT γ-RAY IRRADIATION IN THE LATTICE STRAIN AND IONIC CONDUCTIVITY AT SOLID COMPOSITE OF (LiI)0.5(Al2O3.4SiO2)0.5. The solid composite (LiI)0.5(Al2O3.4SiO2)0.5 has been prepared by solid reaction, by mixing of LiI with Al2O3.4SiO2 powders. The mixture was compacted with diameter 1.5 cm and pressure 5000 psi. The solid composite was irradiated with irradiation dosis 100 kGy, 200 kGy, 300 kGy and 400 kGy. The measurement of crystal structure was done by x-ray diffraction. Result from x-ray diffraction shows that the structure of (LiI)0.5(Al2O3.4SiO2)0.5 was a mixture structure of LiI and Al2O3.4SiO2. The lattice strain of composite (LiI)0.5(Al2O3.4SiO2)0.5 was decrease with increasing radiation doses. The conductivity of composite of (LiI)0.5(Al2O3.4SiO2)0.5 was measured by LCR at frequency between 0.1 Hz to 100 kHz. The result show that the conductivities of composite decrease with increasing radiation doses. Key word: Solid electrolyte, irradiation, x-ray diffraction, conductivity