MODIFIKASI ELEKTRODA PASTA KARBON MENGGUNAKAN KITOSAN UNTUK ANALISIS ION Cd2+ DENGAN ION PENGGANGGU Mn2+ DAN Ni2+ SECARA CYCLIC STRIPPING VOLTAMMETRY MODIFIED CARBON PASTE ELECTRODE USING CHITOSAN FOR ANALYSIS Cd2+ ION WITH DISRUPTORS ION Mn2+ AND Ni2+ IN CYCLIC STRIPPING VOLTAMMETRY

Abstrak. Penelitian ini bertujuan memanfaatkan kitosan yang merupakan pengkhelat ion yang sangat baik untuk menambah sensitivitas elektroda pasta karbon dalam mengkhelat ion logam Cd. Pembuatan elektroda pasta karbon kitosan dengan cara mencampurkan material karbon aktif, minyak parafin, dan kitosan dengan perbandingan 3:2:5, 3:3:4, 3:4:3, dan 3:5:2. Pengukuran menggunakan instrumen voltametri dengan metode cyclic stripiing voltammetry. Komposisi optimum diukur dalam larutan Cd2+ variasi buffer pH 3, 4, 5, dan 6, komposisi optimum yang didapat 3:5:2. Penentuan pH optimum variasi pH 3, 4, 5, dan 6 dengan variasi konsentrasi larutan Cd2+ 5, 10, 20, 40, dan 80 ppm. pH optimum yang diperoleh adalah pH 6 menunjukkan arus puncak Ipc -7.22 mA pada potensial -0.613 V. Kemudian pengukuran waktu deposisi optimum variasi waktu deposisi 0, 10, 20, 40, dan 80 s. Diperoleh waktu optimum 20 s dengan arus puncak Ipc -6.84 mA pada potensial -0.655 V. Kemudian penentuan kecepatan scan optimum variasi scan 0,01; 0,02; 0,04; 0,05; 0,06; dan 0,08 V/s. Diperoleh kecepatan scan optimum pada 0,06 V/s dengan arus puncak Ipc -8.19 mA pada potensial -0.637 V. Kemudian penentuan interferensi ion pengganggu Mn2+ dan Ni2+. Hasil pengukuran larutan Cd2+ tidak diperkenankan ada ion logam lain. Karena dapat mengubah sinyal arus puncak akibat menempelnya ion pengganggu pada permukaan elektroda. Kata kunci: elektroda pasta karbon, voltametri, cyclic stripping voltammetry, arus puncak Ipc Abstract. This research aims to utilize chitosan chelating ion which is very good to increase the sensitivity of the carbon paste electrode in metal ion chelating Cd. Preparation of chitosan-carbon electrode paste by mixing activated carbon material, paraffin oil, and chitosan in the ratio 3:2:5, 3:3:4, 3:4:3, and 3:5:2. Measurements using the method of cyclic voltammetry instrument stripiing voltammetry. The optimum composition was measured in a buffer solution of Cd2+ variations of pH 3, 4, 5, and 6, obtained the optimum composition of 3:5:2. Determination of optimum pH variation of pH 3, 4, 5, and 6 with variation of solution concentration Cd2+ 5, 10, 20, 40, and 80 ppm. The optimum pH was pH 6 obtained showed Ipc -7.22 mA peak current at a potential of -0613 V. Then the optimum deposition time measurement of deposition time variation of 0, 10, 20, 40, and 80 s. The optimum time of 20 s obtained with Ipc -6.84 mA peak current at a potential of -0.655 V. Then the determination of the optimum scan speed of 0.01 scan variation; 0.02; 0.04; 0.05; 0.06; and 0.08 V / s. Optimum scan speed is obtained at 0.06 V / s with a peak current Ipc -8.19 mA at a potential -6.27 V. Then the determination of the interference bullies ions Mn2+ and Ni2+. The results of measurements of Cd2+ solution is not allowed no other metal ions. Since the peak current signal can change due to the attachment of ions on the surface of the electrode bullies. Keywords: carbon paste electrodes, voltammetry, cyclic voltammetry stripping, the peak current Ip