Synthesis and Characterization of Ag/PEDOT:PSS Films Used for NH\(_3\) Selective Sensing

Nano-Ag/PEDOT-PSS films were prepared by spin-coating technique. SEM surface morphology, Raman spectra and gas sensing of methanol, humidity and NH3 were studied. The obtained results showed that the resistance of Ag/PEDOT:PSS sheets exposed to gases related to the generation of electrons from the gases adsorption that eliminated holes as the major carriers in PEDOT:PSS. For NH3 gas the largest change of the resistance of Ag/PEDOT:PSS was observed. The less sensitivity of humidity and ethanol sensing was explained due to less dedoping reaction between H2O and ethanol vapor with Ag/PEDOT:PSS, respectively. This suggests a potential application of the nano-Ag/PEDOT-PSS sensors for the selective monitoring NH3 gas in environment