3D Analyses of crack propagation in torsion

The initiation and propagation of fatigue cracks during cyclic torsion loading was studied in a castAl alloy (A357) with a relatively large (~500 ?m) grain size. 2D observations, revealed that multi site crackinitiation occur on the {111} slip planes exhibiting the highest slip activity (iso-strain Taylor analysis),preferentially on planes nearly perpendicular to the sample axis. Within the first grain, the cracks have apronounced crystallographic propagation mode (mode II crack growth) and strongly interact with the grainboundaries. In situ 3D monitoring of torsion fatigue tests using synchrotron X-ray tomography reveal thatpropagation towards the interior of the samples occurs first along the sample periphery in mode II leading torelatively shallow cracks which penetrate towards the sample center only after a large number of cycles isreached .The values of mode I, II and III stress intensity factors have been calculated from finite elementsimulation at the tip of the shallow mode II crack. Those values are used to analyse the bulk propagation of theobserved cracks