Add to ORKGGlaze in the CaO-MgO-Al2O3-SiO2 system was heated at 950-1190 degrees C for 2 h and characterized. X-ray diffraction showed that only -brace amount of mullite was formed in the glass-ceramic glaze heated at 950 degrees C. Both mullite and alpha-cordierite were formed in the glass-ceramic glaze heated at 1050 degrees C as primary and secondary phases. Glass-ceramic glazes heated at 1120 degrees C and 1190 degrees C contained alpha-cordierite and mullite as major and minor phases. Rietveld analysis revealed that the amount of alpha-cordierite increased and mullite decreased with increasing heating temperature. Field emission scanning electron microscopy showed presence of mullite crystals dispersed within residual glassy phase in the glass-ce...
In tile manufacturing, α-Al₂O₃ is the main type of alumina used in ceramic body and glaze formulatio...
Nepheline-syenite is a fluxing agent used in sanitary ware, electrical porcelain and chinaware bodie...
In tile manufacturing, α-Al₂O₃ is the main type of alumina used in ceramic body and glaze formulatio...
Basic principles of fabricating tile glazes based on cordieritic glass-ceramics are explained. Glass...
In order to verify the possibility to use new glass ceramic materials as glazes for floor tiles, the...
AbstractCordierite based materials are widely used in high temperature applications due to their goo...
In this research a mixture of 90%wt of industrial residues (recycled soda-lime glass and ashes from ...
The formation of ceramic with the prevailing cordierite/mullite in the crystalline phase is greatly ...
The search for effective modifiers of the structure of densely baked cordierite ceramics to reduce t...
Development of ceramics with the prevailing mullite or cordierite crystalline phases is greatly depe...
Glass-ceramics are ceramic materials produced through controlled crystallisation (nucleation and cry...
In order to verify the possibility of using glass-ceramic materials as tile coatings, the devitrific...
The firing process of five raw crystalline frits was investigated by means of DTA, XRD, heating micr...
Microstructural evolution on heating was investigated in a reference industrial composition (50% kao...
In the ceramic tile industry, the change in firing technology from traditional double firing to the ...
In tile manufacturing, α-Al₂O₃ is the main type of alumina used in ceramic body and glaze formulatio...
Nepheline-syenite is a fluxing agent used in sanitary ware, electrical porcelain and chinaware bodie...
In tile manufacturing, α-Al₂O₃ is the main type of alumina used in ceramic body and glaze formulatio...
Basic principles of fabricating tile glazes based on cordieritic glass-ceramics are explained. Glass...
In order to verify the possibility to use new glass ceramic materials as glazes for floor tiles, the...
AbstractCordierite based materials are widely used in high temperature applications due to their goo...
In this research a mixture of 90%wt of industrial residues (recycled soda-lime glass and ashes from ...
The formation of ceramic with the prevailing cordierite/mullite in the crystalline phase is greatly ...
The search for effective modifiers of the structure of densely baked cordierite ceramics to reduce t...
Development of ceramics with the prevailing mullite or cordierite crystalline phases is greatly depe...
Glass-ceramics are ceramic materials produced through controlled crystallisation (nucleation and cry...
In order to verify the possibility of using glass-ceramic materials as tile coatings, the devitrific...
The firing process of five raw crystalline frits was investigated by means of DTA, XRD, heating micr...
Microstructural evolution on heating was investigated in a reference industrial composition (50% kao...
In the ceramic tile industry, the change in firing technology from traditional double firing to the ...
In tile manufacturing, α-Al₂O₃ is the main type of alumina used in ceramic body and glaze formulatio...
Nepheline-syenite is a fluxing agent used in sanitary ware, electrical porcelain and chinaware bodie...
In tile manufacturing, α-Al₂O₃ is the main type of alumina used in ceramic body and glaze formulatio...