Çorum Osmancık Mangan Cevherinin Çeşitli İndirgeyiciler Kullanılarak Sülfürik Asit Çözeltisinde Özütlenmesi

In presented master of science thesis study; it was obtained efficiencies of manganese and iron during leaching of Çorum Osmancık Manganese ore using cane pulp and cotton stalk in sulfuric acid medium. For experimental study, it was determined parameters as leaching temperature, amount of reduction agent, leaching time and acid concentration. Leaching experiments were carried out 40-80 oC temperature, 0-0.1 g reduction agent, 60-360 dk time of leaching and 1-5 M H2SO4 concentration. It was determined experimental points using Box-Wilson experimental design method. Experiments were carried out in thermostatically controlled water bath and concentrations of manganese and iron during the leaching process were measured by Atomin Absorbtion Spectrofotometer (AAS). Leaching efficiency of manganese which was carried out using cotton stalk as a reduction agent is 82 %. In these conditions, efficiency of iron is 38 %.Sunulan yüksek lisans tez çalışmasında; Çorum Osmancık mangan cevherinin pamuk sapı ve şeker pancarı küspesi kullanılarak özütlenmesi sonucunda cevherdeki mangan ve demir verimleri incelenmiştir. Yapılacak deneysel çalışma için değiştirilecek parametreler sıcaklık, indirgeyici miktarı, özütleme süresi ve H2SO4 konsantrasyonu olarak belirlenmiştir. Sıcaklık 40-80 oC aralığında, indirgeyici miktarı 0-0.1 g aralığında, özütleme süresi 60-360 dk aralığında ve H2SO4 konsantrasyonu 1-5 M aralığında olacak şekilde özütleme deneyleri gerçekleştirilmiştir. Box-Wilson deney tasarım yöntemiyle deneylerin hangi noktalarda gerçekleştirileceği belirlenmiştir. Deneyler çalkalayıcılı sıcak su banyosunda gerçekleştirilmiş ve elde edilen örnekler AAS cihazı kullanılarak mangan ve demir miktarları analiz edilmiştir. Pamuk sapıyla gerçekleştirilen özütleme işleminde mangan % 82 verimle kazanılmıştır. Bu koşullarda demir veriminin ise % 38 olduğu bulunmuştur