This in vitro study evaluated the bond and compression strength of cemented leucite reinforced glass ceramics in bovine tooth enamel, comparing three etching times with hydrofluoric acid 10% of the ceramic surface (20, 60 and 90 seconds) and two adhesive treatments (adhesive system + silane and universal adhesive system). For the bond strength test, 120 ceramic cylinders (2mm diameter x 2mm length; n=20) were etched and cemented (80m thick) in enamel with a dual resin cement, varying the adhesive treatment, obtaining the groups: UEXC20s, UEXC60s, UEXC90s, USBU20s, USBU60s, USBU90s. After 24 hours, the shear bond strength test was performed on a universal test machine (0.5mm/min, 50kgf). For the compression test, 30 ceramic plates (5x5mm wit...
The purpose of this research is to evaluate the influence of conditioning time with hydrofluoric aci...
Materiais cerâmicos têm sido utilizados rotineiramente na clínica restauradora. A capacidade de ades...
Orientadores: José Flávio Affonso de Almeida, Caio Cezar Randi FerrazDissertação (mestrado) - Univer...
O objetivo no presente trabalho foi avaliar a resistência da união adesiva de uma cerâmica vítrea (I...
Este estudo in vitro propôs analisar os padrões de condicionamento da superfície da cerâmica a base ...
The aim of this study was to verify through microtensile test the influence of time and concentratio...
Este estudo avalia a resistência de união à microtração de dois cimentos resinosos (RelyXTM U200 - 3...
This study evaluated the tensile bond strength of a resin cement to a ceramic after to three ceramic...
Orientador: Luis Roberto Marcondes MartinsDissertação (mestrado) - Universidade Estadual de Campinas...
O objetivo deste trabalho foi avaliar a resistência de união ao cisalhamento dos cimentos autoadesiv...
The objective of the present study was to evaluate the influence of the conditioning time with 5% an...
The objective of this study to evaluate the effect of universal adhesives application time to enamel...
Trabalho de conclusão de curso (graduação)—Universidade de Brasília, 2017.Objetivo: O presente estud...
A correct surface treatment protocol for ceramics is a very important step in the cementation proces...
O uso da cerâmica é cada vez mais freqüente na odontologia e a estética vem exigindo que a tecnologi...
The purpose of this research is to evaluate the influence of conditioning time with hydrofluoric aci...
Materiais cerâmicos têm sido utilizados rotineiramente na clínica restauradora. A capacidade de ades...
Orientadores: José Flávio Affonso de Almeida, Caio Cezar Randi FerrazDissertação (mestrado) - Univer...
O objetivo no presente trabalho foi avaliar a resistência da união adesiva de uma cerâmica vítrea (I...
Este estudo in vitro propôs analisar os padrões de condicionamento da superfície da cerâmica a base ...
The aim of this study was to verify through microtensile test the influence of time and concentratio...
Este estudo avalia a resistência de união à microtração de dois cimentos resinosos (RelyXTM U200 - 3...
This study evaluated the tensile bond strength of a resin cement to a ceramic after to three ceramic...
Orientador: Luis Roberto Marcondes MartinsDissertação (mestrado) - Universidade Estadual de Campinas...
O objetivo deste trabalho foi avaliar a resistência de união ao cisalhamento dos cimentos autoadesiv...
The objective of the present study was to evaluate the influence of the conditioning time with 5% an...
The objective of this study to evaluate the effect of universal adhesives application time to enamel...
Trabalho de conclusão de curso (graduação)—Universidade de Brasília, 2017.Objetivo: O presente estud...
A correct surface treatment protocol for ceramics is a very important step in the cementation proces...
O uso da cerâmica é cada vez mais freqüente na odontologia e a estética vem exigindo que a tecnologi...
The purpose of this research is to evaluate the influence of conditioning time with hydrofluoric aci...
Materiais cerâmicos têm sido utilizados rotineiramente na clínica restauradora. A capacidade de ades...
Orientadores: José Flávio Affonso de Almeida, Caio Cezar Randi FerrazDissertação (mestrado) - Univer...