Add to ORKGIn this paper, the macroscopic observation and chemical composition analysis of the third crankshaft journal have been carried out. Moreover, macroscopic observation, chemical composition analysis and metallographic analysis were carried out, and were compared with the journal with cracks and without cracks. Based on the experimental results and the causes of crankshaft neck cracks, it can be concluded that the crack form of crankshaft goes along with the grain brittle direction
Based on the analysis of the fracture of a certain type of QT800-2 nodular cast iron crankshaft, the...
Wear as a tribological process has major influence on the reliability and life of engine crankshaft ...
Szczególnym rodzajem zużycia elementów pojazdów są różnego rodzaju uszkodzenia, w tym pęknięcia. W a...
The cause of crankshaft fracture crack of a certain vehicle has been analyzed through macroscopic in...
The cause of crankshaft fracture crack of a certain vehicle has been analyzed through macroscopic in...
The crankshaft of diesel engine of a heavy duty vehicle broke during running. By means of macroscopi...
The cause of crankshaft fracture crack of a certain vehicle has been analyzed through macroscopic an...
Through comprehensive analysis, crack propagated along the nitride in the form of planar clusters, w...
Through comprehensive analysis, crack propagated along the nitride in the form of planar clusters, w...
In this study, failure analysis of a crankshaft was carried out. The crankshaft made of nodular grap...
Study on the fracture specimen of EB03 crankshaft which produced by a crankshaft company. It is foun...
This paper presents the failure analysis of a diesel engine crankshaft used in a truck. An evaluatio...
This paper reports a failure mode analysis of a 1900 cm(3) turbo diesel engine of a well-known comme...
AbstractA failure analysis of two damaged crankshafts are presented: one obtained from a diesel engi...
Wear as a tribological process has major influence on the reliability and life of engine crankshaft ...
Based on the analysis of the fracture of a certain type of QT800-2 nodular cast iron crankshaft, the...
Wear as a tribological process has major influence on the reliability and life of engine crankshaft ...
Szczególnym rodzajem zużycia elementów pojazdów są różnego rodzaju uszkodzenia, w tym pęknięcia. W a...
The cause of crankshaft fracture crack of a certain vehicle has been analyzed through macroscopic in...
The cause of crankshaft fracture crack of a certain vehicle has been analyzed through macroscopic in...
The crankshaft of diesel engine of a heavy duty vehicle broke during running. By means of macroscopi...
The cause of crankshaft fracture crack of a certain vehicle has been analyzed through macroscopic an...
Through comprehensive analysis, crack propagated along the nitride in the form of planar clusters, w...
Through comprehensive analysis, crack propagated along the nitride in the form of planar clusters, w...
In this study, failure analysis of a crankshaft was carried out. The crankshaft made of nodular grap...
Study on the fracture specimen of EB03 crankshaft which produced by a crankshaft company. It is foun...
This paper presents the failure analysis of a diesel engine crankshaft used in a truck. An evaluatio...
This paper reports a failure mode analysis of a 1900 cm(3) turbo diesel engine of a well-known comme...
AbstractA failure analysis of two damaged crankshafts are presented: one obtained from a diesel engi...
Wear as a tribological process has major influence on the reliability and life of engine crankshaft ...
Based on the analysis of the fracture of a certain type of QT800-2 nodular cast iron crankshaft, the...
Wear as a tribological process has major influence on the reliability and life of engine crankshaft ...
Szczególnym rodzajem zużycia elementów pojazdów są różnego rodzaju uszkodzenia, w tym pęknięcia. W a...