Ultralong Organic Phosphorescence in the Solid State: The Case of Triphenylene Cocrystals with Halo- and Dihalo-penta/ tetrafluorobenzene

The polycyclic aromatic hydrocarbon (PAH) triphenylene (TP) has been reacted with halo-pentafluorobenzene (XF5, X = Br, I) and 1,4-dihalo-tetrafluorobenzene (X2F4, X = Br, I) to yield the corresponding cocrystals TP·BrF5, TP·Br2F4, TP·IF5, and TP·I2F4 form I. These materials have been synthesized by dissolving TP into an excess of liquid or molten coformer, and single crystals have been grown via seeding chloroform solutions. They have been fully characterized by a combination of techniques including X-ray diffraction, Raman spectroscopy, and luminescence spectroscopy in the solid state. TP·I2F4 form I was found to undergo a single-crystal to single-crystal (SCSC) polymorphic phase transition induced by temperature (when cooled down to 100 K) leading to the new form TP·I2F4 form II, which is transformed back into the first structure when brought again at RT. This behavior was confirmed also by Raman spectroscopy. Upon cocrystallization and as a result of the external heavy atom effect, all crystalline materials exhibited bright room temperature phosphorescence clearly visible by the naked eye. The latter was almost exclusive for cocrystal TP·I2F4, whereas for TP·Br2F4 both fluorescence and phosphorescence were detected. In TP·Br2F4, the phosphorescence lifetime was on the order of 200 ms, and with the visual outcome of an orange phosphorescence lasting for a couple of seconds upon ceasing the excitation, that makes this compound classifiable as an ultralong organic phosphorescent (UOP) material. The results evidenced the role of the nature of the heavy atom in governing the phosphorescence output from organic cocrystals