Pulse cathodo- and thermoluminescence of alumina ceramic with manganese

Alumina ceramics with manganese in concentration range 0.001-18 wt. % are synthesized. Luminescent properties of obtained ceramics at temperatures 1500-1700°C of sintering in vacuum are investigated. An increase in the manganese concentration leads to quenching of the pulse cathodoluminescence band at 420 nm and the main dosimetric peak at 460 K. The intensity of luminescence in the 676 nm band at manganese concentrations of more than 1 wt. % and the TL yield for all the observed peaks increase when annealing temperature rises. Sublinear increase in TL intensity with a growing dose is observed in the range of 3-1000 Gy in 460 and 620 K peaks. © Published under licence by IOP Publishing Ltd.The reported study was funded by RFBR according to the research project № 18-33-00085