SAXS study of the micro-inhomogeneity of industrial soda lime silica glass

The microstructure of a variety of industrial multicomponent soda lime glasses for container and glazing and of a lead alkali silicate glass for pressed tableware articles was analyzed using small angle X-ray scattering (SAXS). No inhomogeneity with size >0.5 nm was found in the industrial samples, while ternary soda lime glass samples with a suitable composition when heat treated developed a phase separation which SAXS detected without difficulty. The results obtained disprove earlier reports which attributed problems of rheology and strength affecting container production ('bad workability') to microstructure formation. © 1994