Influence of samarium ions (Sm3+) on the optical properties of lithium zinc phosphate glasses

New glass samples with composition xSm2O3-(15-x) Li2O-45ZnO-40P2O5, where x=0, 0.1, 0.3 and 0.5 mol % are prepared by conventional melt-quenching method. X-ray Diffraction measurements were performed to confirm their amorphous nature. Densities of these glasses were measured by Archimedes method. Optical properties were studied using optical absorption spectra which was recorded at room temperature in the UV-Vis region. Electronic transitions specific to the rare earth ion were observed from the UV-Visible spectroscopy. Optical direct band gap and indirect band gap energies were measured and their values were found to be between 4.23-4.74 eV and 3.02-3.67 eV, respectively. Refractive index has been measured with respect to different concentrations of Sm2O3. Polaron radius, inter-nuclear distance, field strength, dielectric constant and polarizability of oxide ions have been calculated. Fluorescence spectroscopy measurements have been performed by excitation in the UV-Visible range, which resulted in the significant fluorescence peaks. The luminescence color of the glass system has been characterized using Commission International de l’Eclairage de France 1931 chromaticity diagram