Self-assembly of silicon-containing triblock copolymer and terpolymers

Thesis: S.M., Massachusetts Institute of Technology, Department of Materials Science and Engineering, 2019Cataloged from PDF version of thesis.Includes bibliographical references.The block copolymer (BCP) self-assembly has garnered significant interest due to its ability to generate periodic nanostructures with a variety of morphologies. Compared to diblock copolymers that have been extensively studied to form the conventional morphologies such as spheres, cylinders, and lamellae depending on the block volume fraction, more complex polymer architectures are expected to offer additional degrees of freedom and a wider range of structures. Solvent vapor annealing (SVA) using a continuous gas flow system allows a precise control over the annealing condition, which can capture intermediate morphologies including perforated lamellae and gyroids and can create unique nanostructures that have not been observed in diblock copolymers. Combining with self-consistent field theory (SCFT) modeling and in situ grazing-incidence small-angle X-ray scattering (GISAXS) measurement, the phase behavior of advanced polymer architectures can be revealed in details.Here, the self-assembly behavior of silicon-containing triblock copolymer and terpolymers in multi-layered films under SVA is presented. Using both experimental and SCFT approaches, the phase behavior of poly(stryrene-b-dimethylsiloxane-b-styrene) (PS-b-PDMS-b-PS or SDS32) thin films was investigated as a function of the as-cast film thickness and the ratio of two different solvent vapors, toluene and heptane. In comparison with diblock PS-b-PDMS with same molecular weight, the SDS32 offers a simple route to produce a diversity of well-ordered bilayer structures with smaller feature sizes, including the formation of bilayer perforated lamellae over a large process window. In addition, the morphological evolution of core-shell cylinder-forming triblock terpolymers during SVA was monitored in situ using GISAXS. A reversible order-order phase transformation between spheres and cylinders occurred during the annealing process.One of the final morphologies consisted of the regions of in-plane cylinders, with the majority of the film comprising vertical core-shell cylinders passing through perforated lamellae of poly 1,1-dimethyl silacyclobutane (PDMSB).by Sangho Lee.S.M.S.M. Massachusetts Institute of Technology, Department of Materials Science and Engineerin