Tensile and flexural properties of hybrid graphene oxide/epoxy carbon fibre reinforced composites.

In this study, nano-sized graphene oxide sheets were homogenously dispersed via sonication methods in epoxy followed by vacuum resin infusion for the fabrication of the epoxy, graphene oxide (GO) and micro-sized carbon fibre reinforced nanocomposites (EP/CF/GO). Graphene oxide concentrations ranging from 0.1 - 0.5 wt. % were studied to investigate the effect on tensile and flexural strength. It was observed that the tensile strength of the EP/CF decreased with the addition of GO but increased with GO weight concentration in the nanocomposites studied from 498MPa to 519 MPa for the inclusion of 0.1 to 0.5 wt.% GO respectively. The 0.5 wt. % EP/CF/GO recorded a 10% increase in Young's modulus compared to the classical epoxy / carbon fibre composites, and similar trend was observed for the flexural properties. However flexural strength of the GO samples did not surpass the control sample (epoxy /carbon fibre composites) with the 0.3 wt.% GO samples (EP/CF/GO) providing the greatest flexural strength of >580 MPa compared to the 0.1 wt.% and 0.5 wt.% GO samples