Influencia del hollín sobre la resistencia a la compresión de ladrillos cerámicos

This article presents the results obtained in the mechanical properties of the addition of soot, which is a byproduct of cooking the bricks used in Santander brickworks. The clay used was initially characterized using the manual granulometric method, following the NSR 10 standard. Chemical and mineralogical compositions were analyzed using a X- ray Diffraction technique. The analysis of the mechanical properties of ceramic was developed through compression tests, according to the guidelines of the Colombian NTC: 4017 Technical Standard. The results show that adding less than 60% in mass of soot residues, when clay is added, increases the compressive strength to 265.31 kg / cm2 in average. This increase is significant taking into account that the minimum compression value according to the standard is 140 kgf/cm2.Este artículo presenta los resultados obtenidos en las propiedades mecánicas de la adición del hollín, el cual es un subproducto de la cocción de los ladrillos usados en las ladrilleras de Santander. La arcilla usada inicialmente fue caracterizada por el método granulométrico manual siguiendo la norma NSR 10. Las composiciones químicas y mineralógicas se analizaron por medio de la técnica de Difracción de Rayos - X). El análisis de las propiedades mecánicas de los cerámicos se desarrolló mediante el ensayo de compresión según los lineamientos de la Norma Técnica Colombiana NTC: 4017. Los resultados muestran que la adición menor a 60 % en masa de residuos de hollín cuando se adiciona a la arcilla aumenta la capacidad de resistencia a la compresión en un valor promedio de 265.31 kgf/cm2; este aumento es significativo ya que el valor mínimo a la compresión según la norma es de 140 kgf/cm2