Dielectric properties of poly (vinyl alcohol) hydrogels prepared by freezing / thawing technique

The dielectric behavior of poly (vinyl alcohol) -PVA- crosslinked hydrogels obtained by the repeated freezing/ thawing (F/T) technique have been investigated by dielectric relaxation spectroscopy (DRS) and differential scanning calorimetry (DSC). The crosslinked polymer is produced by the clustering of chains caused by the association of a polar group of the dissolved polymer followed by polymer crystallization. The dielectric spectra obtained from -50 °C to -10 °C show a broad secondary relaxation process associated to local mobility, ß relaxation, which is related to the terminal polar groups (OH). This process is strongly affected by the freezing/thawing cycles applied. The values of tan δ are below 1 indicating the dielectric phenomenon is predominant in all samples. The effect of crosslinking PVA on the dynamics of the secondary relaxation process was further analyzed.Por médio de espectroscopia dielétrica (DRS) e calorimetria diferencial de varredura (DSC) pesquisaramse as propriedades dielétricas dos hidrogeis de álcool polivinílico -PVA- entrecruzados por ciclos repetidos da técnica congelamento/descongelamento. A associação dos grupos polares do polímero dissolvido seguida de sua cristalização produz a reticulação do polímero. A espectroscopia dielétrica obtida entre -50 °C e -10 °C demonstrou a existência de um processo de relaxação secundário associado com a mobilidade de grupos laterais polares OH da corrente principal, a relaxação β. Os ciclos de congelamento/descongelamento afetam fortemente este processo. O fenômeno dielétrico predomina em todas as mostras como o evidência o valor menor de 1 de tan δ. Ademais, analisou-se o efeito do entrecruzamento na dinâmica da relaxação secundária.Por medio de espectroscopia dieléctrica (DRS) y calorimetría diferencial de barrido (DSC) se investigaron las propiedades dieléctricas de los hidrogeles de alcohol polivinílico -PVA- entrecruzados por ciclos repetidos de la técnica congelamiento/descongelamiento. La asociación de los grupos polares del polímero disuelto seguida de su cristalización produce la reticulación del polímero. La espectroscopia dieléctrica obtenida entre -50 °C y -10 °C demostró la existencia de un proceso de relajación secundario asociado con la movilidad de grupos laterales polares OH de la cadena principal, la relajación β. Los ciclos de congelamiento/descongelamiento afectan fuertemente este proceso. El fenómeno dieléctrico predomina en todas las muestras como lo evidencia el valor menor de 1 de tan δ. Además, se analizó el efecto del entrecruzamiento en la dinámica de la relajación secundaria