Microdureza de la superaleación nickelvac (n-90) manufacturada por pulvimetalurgia

Through powder metallurgy it was fabricated the nickelvac alloy, which is a superalloy mainly made by nickel. The fabricated alloy was homogenized at two different temperatures (1000 and 1065 °C during 2h) and later aged at 350°C during different times (0.5, 1, 2, and 3 h). From microhardness measurements realized in the samples, it was determined that the more time of aged meet, the more hardness reflected. From microstructure observations made by scanning electron microscopy, it was determined the formation of NixTiy-type precipitates, being these responsible for the microhardness improvement of the made alloy, these precipitates have their origin during the alloy aged.A través de la técnica de metalurgia de polvos se fabricó la aleación denominada comercialmente como nickelvac (N-90), que se trata de una superaleación hecha principalmente a base de níquel. La aleación fabricada fue sometida primeramente a un proceso de homogenizado a dos temperaturas distintas (1000 y 1065°C durante 2 h) y posteriormente fue envejecida a 350°C durante diferentes tiempos (0.5, 1, 2 y 3 h). De las mediciones de microdureza realizadas en las diferentes muestras, se obtuvo que mayores tiempos de envejecido reflejan mayores valores de dureza. De las observaciones de la microestructura con ayuda de microscopía electrónica de barrido, se pudo determinar la formación de precipitados del tipo NixTiy, siendo estos los causantes de los incrementos en la dureza de la aleación, estos precipitados tienen su origen durante el envejecido de la aleación