Effects of irradiation on intergranular stress corrosion cracking of Type 304 stainless steel

Constant extension rate tests (CERT) were run on ten irradiated specimens in continuation of a study of environmental effects on intergranular stress corrosion cracking of type 304 stainless steel. Specimens of both furnace sensitized and annealed material were irradiated to fluences of 1 to 2 {times} 10{sup 21} neutrons (E {ge} 0.1 Mev) per square centimeter at a temperature of {approximately}150{degree}C in a reflector position of the High Flux Isoptope Reactor at ORNL. CERT test conditions duplicated conditions for testing of non-irradiated specimens. The time-to-failure for the sensitized and irradiated specimens showed the same pattern of dependence on test variables as the non-irradiated specimens in an associated study. The annealed and irradiated specimens showed no evidence of irradiation assisted stress corrosion cracking