SLUDGE BATCH VARIABILITY STUDY WITH FRIT 418

The Defense Waste Processing Facility (DWPF) initiated processing Sludge Batch 6 (SB6) in the summer of 2010. In support of processing, the Savannah River National Laboratory (SRNL) provided a recommendation to utilize Frit 418 to process SB6. This recommendation was based on assessments of the compositional projections for SB6 available at the time from the Liquid Waste Organization (LWO) and SRNL (using a model-based approach). To support qualification of SB6, SRNL executed a variability study to assess the applicability of the current durability models for SB6. The durability models were assessed over the expected Frit 418-SB6 composition range. Seventeen glasses were selected for the variability study based on the sludge projections used in the frit recommendation. Five of the glasses are based on the centroid of the compositional region, spanning a waste loading (WL) range of 32 to 40%. The remaining twelve glasses are extreme vertices (EVs) of the sludge region of interest for SB6 combined with Frit 418 and are all at 36% WL. These glasses were fabricated and characterized using chemical composition analysis, X-ray diffraction (XRD) and the Product Consistency Test (PCT). After initiating the SB6 variability study, the measured composition of the SB6 Tank 51 qualification glass produced at the SRNL Shielded Cells Facility indicated that thorium was present in the glass at an appreciable concentration (1.03 wt%), which made it a reportable element for SB6. This concentration of ThO{sub 2} resulted in a second phase of experimental studies. Five glasses were formulated that were based on the centroid of the new sludge compositional region combined with Frit 418, spanning a WL range of 32 to 40%. These glasses were fabricated and characterized using chemical composition analysis and the PCT. Based on the measured PCT response, all of the glasses (with and without thorium) were acceptable with respect to the Environmental Assessment (EA) reference glass regardless of thermal history. All of the normalized boron releases were less than 1 g/L. While all of the targeted glass compositions were predictable with respect to the Product Composition Control System (PCCS) models for durability, a small number of the measured glass compositions were located outside of the lower prediction limit indicating poorer durability than what was actually measured. These unpredictable glasses were in the same lithium metaborate (LM) preparation block during the chemical analyses, which resulted in measured compositions that were not representative of the target compositions. A review of the data did not indicate a clear cause for the problem. Re-digestion and re-measurement of three glasses from this preparation block yielded glass compositions closer to the target values and predicted PCT responses within the PCCS model uncertainty. Therefore, it is believed that the glasses were correctly fabricated and the targeted compositions are closer representations of the true compositions. Per the requirements of the DWPF Glass Product Control Program, the PCCS durability models have been shown to be applicable for the SB6/Frit 418 glass system. PCT results from the glasses fabricated as part of the variability study were shown to be predictable and/or acceptable with respect to the DWPF PCCS models. In addition, the inclusion of ThO{sub 2} was shown to have minimal impact on the acceptability and predictability of the variability study glasses