Structure of CdTe/ZnTe superlattices

The structure of CdTe/ZnTe superlattices has been analyzed through θ/2θ x‐ray diffraction, photoluminescence, and in situ reflection high‐energy electron diffraction (RHEED) measurements. Samples are found to break away from Cd_(x)Zn_(1−x)Te buffer layers as a consequence of the 6% lattice mismatch in this system. However, defect densities in these superlattices are seen to drop dramatically away from the buffer layer interface, accounting for the intense photoluminescence and high‐average strain fields seen in each of our samples. Observed variations in residual strains suggest that growth conditions play a role in forming misfit defects. This could explain discrepancies with calculated values of critical thickness based on models which neglect growth conditions. Photoluminescence spectra reveal that layer‐to‐layer growth proceeded with single monolayer uniformity, suggesting highly reproducible growth. Our results give hope for relatively defect‐free Cd_(x)Zn_(1−x)Te/Cd_(y)Zn_(1−y)Te superlattices with the potential for applications to optoelectronics offered by intense visible light emitters