Add to ORKGZSM-5 membranes with good permeation selectivity for n-butane–isobutane are grown hydrothermally from a clear solution on horizontally-held porous α-Al_2O_3 disks
This thesis is devoted to illustrate the preparation of MFI-type engineered supported zeolite membra...
This paper presents a study of MFI-type zeolite crystal growth during hydrothermal synthesis of nano...
Thesis (M.Sc. (Pharmaceutical Chemistry))--North-West University, Potchefstroom Campus, 2006.Hydroxy...
ZSM-5 membranes with good permeation selectivity for n-butane–isobutane are grown hydrothermally fro...
Zeolite ZSM-5 membranes were grown on porous α-Al_2O_3 disks by in-situ hydrothermal synthesis at 17...
Zeolite ZSM-5 membranes with high n-butane:isobutane selectivities, e.g., 322 at 185°C, are obtained...
The work presented in this thesis was aimed to synthesize zeolite films in the absence of organic ad...
Zeolite ZSM-5 membranes were prepared by in situ crystallization on porous α-Al_2O_3 disks that cont...
Thin (2-7 μm) polycrystalline randomly-oriented zeolite MFI membranes were prepared on an α-Al2O3 su...
Thin (2–7 μm) polycrystalline randomly-oriented zeolite MFI membranes were prepared on an -Al2O3 sup...
ZSM-5 zeolite membranes synthesized on rough porous α-Al2O3 tubes with an average pore size of 2 μm ...
AbstractPresent work analyses the effect produced by the presence of ZSM-5 zeolite in an alumina tub...
The zeolite membrane of MFI could be sinthesized on alpha alumina support having an asymmetric struc...
Zeolite ZSM-5 particles formed in the synthesis solution assume a negative charge due to electrical ...
Zeolite films are sought as components of molecular sieve membranes. Different routes used to prepar...
This thesis is devoted to illustrate the preparation of MFI-type engineered supported zeolite membra...
This paper presents a study of MFI-type zeolite crystal growth during hydrothermal synthesis of nano...
Thesis (M.Sc. (Pharmaceutical Chemistry))--North-West University, Potchefstroom Campus, 2006.Hydroxy...
ZSM-5 membranes with good permeation selectivity for n-butane–isobutane are grown hydrothermally fro...
Zeolite ZSM-5 membranes were grown on porous α-Al_2O_3 disks by in-situ hydrothermal synthesis at 17...
Zeolite ZSM-5 membranes with high n-butane:isobutane selectivities, e.g., 322 at 185°C, are obtained...
The work presented in this thesis was aimed to synthesize zeolite films in the absence of organic ad...
Zeolite ZSM-5 membranes were prepared by in situ crystallization on porous α-Al_2O_3 disks that cont...
Thin (2-7 μm) polycrystalline randomly-oriented zeolite MFI membranes were prepared on an α-Al2O3 su...
Thin (2–7 μm) polycrystalline randomly-oriented zeolite MFI membranes were prepared on an -Al2O3 sup...
ZSM-5 zeolite membranes synthesized on rough porous α-Al2O3 tubes with an average pore size of 2 μm ...
AbstractPresent work analyses the effect produced by the presence of ZSM-5 zeolite in an alumina tub...
The zeolite membrane of MFI could be sinthesized on alpha alumina support having an asymmetric struc...
Zeolite ZSM-5 particles formed in the synthesis solution assume a negative charge due to electrical ...
Zeolite films are sought as components of molecular sieve membranes. Different routes used to prepar...
This thesis is devoted to illustrate the preparation of MFI-type engineered supported zeolite membra...
This paper presents a study of MFI-type zeolite crystal growth during hydrothermal synthesis of nano...
Thesis (M.Sc. (Pharmaceutical Chemistry))--North-West University, Potchefstroom Campus, 2006.Hydroxy...