Enhancing the catalytic activity of Ru NPs deposited with carbon species in yolk-shell nanostructures

The synthesis of metal NPs with a well-defined size, shape and composition provides opportunities for tuning the catalytic performance of metal NPs. However, the presence of a stabilizer on the metal surface always blocks the active sites of metal NPs. Herein, we report an efficient method to remove the stabilizer on the metal surface via H-2 pyrolysis with Ru-poly(amindoamine) encapsulated in silica-based yolk-shell nanostructures as an example. The CO uptake amount of Ru NPs increases sharply after H-2 pyrolysis, indicating that the exposure degree of Ru NPs is increased. No aggregation of the colloidal Ru NPs occurs after H-2 pyrolysis, which could be mainly assigned to the protection effect of C and N species formed on Ru NPs. The overall activity of Ru NPs in the yolk-shell nanostructure after the pyrolysis could reach as high as 20 300 mmol per mmol Ru per h in the hydrogenation of toluene, which is much higher than that of most reported Ru-based solid catalysts. It was found that the yolk-shell nanostructure could efficiently prevent the leaching of Ru NPs during the catalytic process. Ru NPs in the yolk-shell nanostructure could also catalyze the hydrogenation of benzoic acid and Levulinic acid with high activity and selectivity