Add to ORKGThe quench sensitivity of AA7136 has been experimentally investigated using Jominy end quench and test coupons of various heat treatments. It was found that this alloy is not quench sensitive. In addition, the effects of heating rate on both solution and aging treatments on AA7136 and AA7075 were determined using a newly developed reverse Jominy heating test. It was observed that hardness was reduced after rapid heating during aging and hardness increased slightly after rapid heating during solutionizing. These results are discussed in terms of microstructural developments
High strength aluminum alloys are recently widely used in aircraft, automobile and construction indu...
textThe retrogression-reaging (RRA) and hot forming behavior of AA7075 were studied. AA7075 is a hig...
The precipitation behaviour during cooling from solution annealing of high alloyed aluminium alloy 7...
The quench sensitivity of AA7136 has been experimentally investigated using Jominy end quench and te...
The use of AA6xxx series alloys continues to grow with the increasing demand for more fuel efficie...
The purpose of this experimental project was to design, construct, and validate a high-resolution ap...
Mechanical property variation across the cross section of heat treatable aluminum alloys is a major ...
Aluminum and steel components are usually quenched in forced gas, oil or water flow to improve mecha...
peer-reviewedDetermination of the time-temperature property C curve for aluminium alloys usually inv...
peer-reviewedWhen quenching heat treatable aluminium alloys, the interior of a sample cools at a dif...
New generations of high strength aluminum alloys are increasingly used in automotive industry. AA707...
The effects of heat treating process parameters on the microstructure, residual stress, and distorti...
The performance of a series of mineral oil based quenchants has been investigated using the CHTE Que...
This work presents the experimental results concerning the behavior on heat treatment of on aluminum...
The innovative solution heat treatment, forming and in-die quenching (HFQ) processcombines die formi...
High strength aluminum alloys are recently widely used in aircraft, automobile and construction indu...
textThe retrogression-reaging (RRA) and hot forming behavior of AA7075 were studied. AA7075 is a hig...
The precipitation behaviour during cooling from solution annealing of high alloyed aluminium alloy 7...
The quench sensitivity of AA7136 has been experimentally investigated using Jominy end quench and te...
The use of AA6xxx series alloys continues to grow with the increasing demand for more fuel efficie...
The purpose of this experimental project was to design, construct, and validate a high-resolution ap...
Mechanical property variation across the cross section of heat treatable aluminum alloys is a major ...
Aluminum and steel components are usually quenched in forced gas, oil or water flow to improve mecha...
peer-reviewedDetermination of the time-temperature property C curve for aluminium alloys usually inv...
peer-reviewedWhen quenching heat treatable aluminium alloys, the interior of a sample cools at a dif...
New generations of high strength aluminum alloys are increasingly used in automotive industry. AA707...
The effects of heat treating process parameters on the microstructure, residual stress, and distorti...
The performance of a series of mineral oil based quenchants has been investigated using the CHTE Que...
This work presents the experimental results concerning the behavior on heat treatment of on aluminum...
The innovative solution heat treatment, forming and in-die quenching (HFQ) processcombines die formi...
High strength aluminum alloys are recently widely used in aircraft, automobile and construction indu...
textThe retrogression-reaging (RRA) and hot forming behavior of AA7075 were studied. AA7075 is a hig...
The precipitation behaviour during cooling from solution annealing of high alloyed aluminium alloy 7...