Utjecaj nanočestica titanova dioksida i nanočestica boron nitrida na mehanička, morfološka i toplinska svojstva WF/PP kompozita

This study evaluated the effect of nano boron nitride (BN) and nano titanium dioxide (TiO2 ) on some physical, mechanical and thermal properties of WF/PP composites. Polyproplene as a polymer matrix and wood flour obtained from particleboards were used as reinforcing fillers to prepare the composites by using a single screw extruder. It was observed that density in all composites did not change significantly with the increasing of wood flour. It was found that BMOR and BMOE of the composites increased with the increasing of the wood flour content and nanoparticle types, while the TMOR and TMOE decreased. According to the results of thermal properties (TGA), thermal degradation of all composites was found to be lower compared with pure PP.U radu je predočeno istraživanje utjecaja nanočestica borova nitrida (BN) i nanočestica titanova dioksida (TiO2 ) na neka fi zikalna, mehanička i toplinska svojstva drvno-plastičnih kompozita (WF/PP kompozita). Za proizvodnju kompozita upotrijebljeni su polipropilen kao polimerna matrica i drvno brašno dobiveno od ploča iverica kao punilo, uz pomoć jednovijčanog ekstrudera. Uočeno je da se gustoća kompozita ne mijenja značajno s povećanjem količine drvnog brašna. Utvrđeno je da se BMOR i BMOE kompozita povećava s povećanjem sadržaja drvnog brašna i nanočestica TiO2 i BN-a, dok se TMOR i TMOE smanjuju. Prema rezultatima istraživanja toplinskih svojstava (TGA), zaključeno je da je toplinska degradacija svih istraživanih kompozita manja u usporedbi s čistim polipropilenom