Utjecaj toplinske obrade na mikrostrukturu i mehanička svojstva legure Cu-Al-Mn s prisjetljivosti oblika

The 8-mm diameter bars of Cu-Al-Mn shape memory alloys were produced by continuous casting technique. The samples were characterised using optical microscopy and scanning electron microscopy along with EDX analysis. The continuous cast alloy revealed some martensitic phase, which, after quenching, led to the microstructure that is completely martensite. Quenching of samples had an effect on several mechanical properties and change in morphology of fracture. After ageing at 200 °C and 300 °C, the tensile strength increased and elongation drastically decreased. Morphology of fracture surface changed from primary ductile to a mixture of intergranular and ductile. This work is licensed under a Creative Commons Attribution 4.0 International License.Šipke promjera 8 mm proizvedene su iz legure Cu-Al-Mn s prisjetljivosti oblika tehnikom kontinuiranog lijevanja. Uzorci su karakterizirani pomoću optičke mikroskopije i pretražne elektronske mikroskopije uz analizu EDX. Kontinuirano lijevana legura je pokazala mjestimičnu prisutnost martenzitne faze, dok je nakon kaljenja nastala potpuno martenzitna mikrostruktura. Kaljenje uzoraka utjecalo je na mehanička svojstva i na promjenu morfologije prijeloma. Nakon starenja pri 200 °C i 300 °C porasla je vlačna čvrstoća a izduženje se drastično smanjilo. Morfologija prijelomne površine se mijenjala od duktilne do mješavine interkristalne i duktilne. Ovo djelo je dano na korištenje pod licencom Creative Commons Imenovanje 4.0 međunarodna