Procjena mikropropusnosti zubnih korijena obrađenih s eksperimentalnim endodontskim kompozitom

This study compares the apical microleakage (ML) of an experimental amorphous calcium phosphate (ACP) endodontic sealer with the ML of a commercial material with similar resin composition (Resilon). The penetration of the methylene blue dye solution following 72 h immersion at 37 °C was measured in root canals of single-rooted human teeth treated with: 1) experimental primers or Resilon primer, 2) experimental ACP selaer or Resilon sealer, and 3) Gutta-perha or Resilon filler. The results contradict the reported ability of Resilon to provide an almost hermetic seal or perform better than gutta-percha. The ML values obtained with ACP sealant (equal to or up to 16 % lower than the ML values in Resilon groups) merit further evaluation of this experimental material.U radu je uspoređena mikropropusnost (ML) experimentalnoga endodontskog kompozita temeljenoga na amorfnom kalcijevom fosfatu s mikropropusnosti komercijalnoga materijala sa sličnim sastavom smole (Resilon). Mjereno je prodiranje metilenskog plavila u zubima uronjenim u otopinu boje 72 sata pri temperaturi 37o C. Korijeni su zuba obrađeni: 1) eksperimentalnim primerima ili Resilon primerom, 2) s eksperimentalnim ACP ili Resilon brtvilom, te 3) gutaperkom ili Resilon punilom. Rezultati su u suprotnosti s tvrdnjama drugih autora da Resilon hermetički zabrtvljuje kanal korijena zuba i da bolje ispunjava kanal od gutaperke. Vrijednosti ML-a s ACP brtvilom (jednake ili do 16% niže od vrijednosti ML-a u skupinama s Resilonom) ukazuju da je vrijedno nastaviti testiranje ACP experimentalnoga kompozita za endodontsku uporabu