Vliv obsahu boru na elektrochemické vlastnosti borem dopovaných diamantových elektrod a jejich využití pro stanovení leukovorinu.

Set of the lab-made boron-doped diamond electrodes (BDDEs) prepared with various B/C ratio (1000, 2000, 4000, 8000, 10,000, and 20,000 ppm) in the gas phase was subjected to the detailed characterization in the present paper. It was proved, that the B/C ratio influenced the electrochemical features of the working electrodes like a width of the potential window, which decreased with increasing B/C. Variations of reversibility of two redox systems (Fe(CN)63−/4− and Ru(NH3)62+/3+) depending on B/C were observed as well. The best electrochemical properties were found for BDDE with B/C 10000 ppm. Moreover, the working electrodes were tested for voltammetric analysis of leucovorin based on its oxidation. The lab-made BDDEs were applied for voltammetric analysis of the pharmaceutical preparation containing leucovorin with excellent results (recovery 97.7–103.3%, RSD5 ≤ 2.1%).Předmětem této studie byla detailní charakterizace řady borem dopovaných diamantových elektrod (BDDE) připravených s různým poměrem B/C (1000, 2000, 4000, 8000, 10 000 a 20 000 ppm) v plynné fázi. Bylo zjištěno, že B/C ovlivňuje elektrochemické vlastnosti elektrod jako jsou šířka využitelného potenciálového okna, které se zužuje s rostoucím obsahem boru. Rovněž byla pozorována změna reverzibility redoxních systémů (Fe(CN)63−/4− and Ru(NH3)62+/3+) v závislosti na B/C. Nejlepší elektrochemické vlastnosti vykazovala BDDE s poměrem B/C 10 000 ppm. Navíc byly testované elektrody aplikovány při voltametrické analýze leukovorinu založené na jeho oxidaci. Laboratorně připravené BDDE poskytovaly velmi dobré výsledky i při analýze farmaceutických přípravků (výtěžnost 97,7-103,3 %, RSD5 ≤ 2.1%