High Temperature Corrosion Resistance of Coatings Deposited by Hvof for Application in Steam Turbines

AbstractThe geothermal steam turbines are exposed to mechanisms of corrosion/erosion that weakens its components and reduces their useful life. Due to this problem work has been done in application and characterization of coating in solid state by means of the technique of high-velocity Oxygen Fuel (HVOF), evaluating the corrosion rate (Vcorr) at high temperature of MCrAlY and Diamalloy 4006 coatings deposited on stainless steel SS304. Test was performance in an Autoclave at 1700C using a modified geothermal fluid as electrolyte. Open circuit potential was monitoring during 24hours until the system reached the equilibrium. After that, Polarization and Impedance Spectroscopy techniques were used to evaluate the specimens. For microstructure characterization; X–ray Diffraction (XRD), electron sweep microscope (SEM) and Optical microscope were applied. Results show that both coatings (Diamalloy 4006 and MCrAlY), have low current density compare with the substrate, which is an indicative of a lower corrosion rate due to the passive behavior of the species deposited on the Surface of the coating